Sulfite process

The sulfite process produces wood pulp which is almost pure cellulose fibers by using various salts of sulfurous acid to extract the lignin from wood chips in large pressure vessels called digesters. The salts used in the pulping process are either sulfites (SO32−), or bisulfites (HSO3−), depending on the pH. The counter ion can be sodium (Na+), calcium (Ca2+), potassium (K+), magnesium (Mg2+) or ammonium (NH4+).

History

The use of wood to make pulp for paper began with the development of mechanical pulping in Germany by F.G. Keller in the 1840s.[1] Chemical processes quickly followed, first with J. Roth's use of sulfurous acid to treat wood, followed by Benjamin Chew Tilghman's US patent on the use of calcium bisulfite, Ca(HSO3)2, to pulp wood in 1867.[2] Almost a decade later in 1874 the first commercial sulfite process|sulfite pulp mill was built in Sweden. It used magnesium as the counter ion and was based on work by Carl Daniel Ekman.

By 1900 sulfite pulping had become the dominant means of producing wood pulp, surpassing mechanical pulping methods. The competing chemical pulping process, the sulfate or kraft process was developed by Carl F. Dahl in 1879 and the first kraft mill started (in Sweden) in 1890.[2] The first sulphite mill in the United States was the Richmond Paper Company in Rumford, Rhode Island in the mid-1880s. The invention of the recovery boiler by G.H. Tomlinson in the early 1930s [1] allowed kraft mills to recycle almost all of their pulping chemicals. This, along with the ability of the kraft process to accept a wider variety of types of wood and produce stronger fibers [3] made the kraft process the dominant pulping process starting in the 1940s.[2] Sulfite pulps now account for less than 10% of the total chemical pulp production[2] and the number of sulfite mills continues to decrease.[4][5][6]

Magnesium was the standard counter ion until calcium replaced it in the 1950s.

Processes involved in sulfite pulping

Pulping liquor preparation

The pulping liquor for most sulfite mills is made by burning sulfur with the correct amount of oxygen to give sulfur dioxide, which is then absorbed into water to give sulfurous acid.

S + O2 → SO2
SO2 + H2O ⇌ H2SO3

Care must be taken to avoid the formation of sulfur trioxide since it gives undesired sulfuric acid when it is dissolved in water.

2 SO2 + O2 → 2SO3
SO3 + H2O ⇌ H2SO4

Sulfuric acid is undesirable since it promotes hydrolysis of cellulose without contributing to delignification.

The cooking liquor is prepared by adding the counter ions as hydroxides or carbonates. The relative amounts of each species present in the liquid depend largely on the relative amounts of sulfurous used. For monovalent (Na+, K+ and NH4+) hydroxides, MOH:

H2SO3 + MOH → MHSO3 + H2O
MHSO3 + MOH → M2SO3 + H2O

For divalent (Ca2+, Mg2+) carbonates, MCO3:

MCO3 + 2H2SO3 → M(HSO3)2 + CO2 + H2O
M(HSO3)2 + MCO3 → 2 MSO3 + CO2 + H2O

Pulping

Sulfite pulping is carried out between pH 1.5 and 5, depending on the counterion to sulfite (bisulfite) and the ratio of base to sulfurous acid. The pulp is in contact with the pulping chemicals for 4 to 14 hours and at temperatures ranging from 130 to 160 °C (266 to 320 °F), again depending on the chemicals used.

Most of the intermediates involved in delignification in sulfite pulping are resonance-stabilized carbocations formed either by protonation of carbon-carbon double bonds or acidic cleavage of ether bonds which connect many of the constituents of lignin. It is the latter reaction which is responsible for most lignin degradation in the sulfite process.[1] The electrophilic carbocations react with bisulfite ions (HSO3−)to give sulfonates.

R-O-R' + H+ → R+ + R'OH
R+ + HSO3− → R-SO3H

The sulfite process does not degrade lignin to the same extent that the kraft process does and the lignosulfonates from the sulfite process are useful byproducts.

Chemical recovery

The spent cooking liquor from sulfite pulping is usually called brown liquor, but the terms red liquor, thick liquor and sulfite liquor are also used (compared to black liquor in the kraft process). Pulp washers, using countercurrent flow, remove the spent cooking chemicals and degraded lignin and hemicellulose. The extracted brown liquor is concentrated, in multiple effect evaporators. The concentrated brown liquor can be burned in the recovery boiler to generate steam and recover the inorganic chemicals for reuse in the pulping process or it can be neutralized to recover the useful byproducts of pulping. Recent developments in Chemrec's black liquor gasification process, adapting the technology to use in the sulfite pulping process, could make second generation biofuels production an alternative to the conventional recovery boiler technology.[7]

The sulfite process can use calcium, ammonium, magnesium or sodium as a base.

Calcium-based

The earliest process used calcium, obtained as inexpensive calcium carbonate and there was little incentive to recover the inorganic materials.

Ammonia-based

Ammonia-based processes do not allow recovery of the pulping chemicals since ammonia or ammonium salts are oxidized to nitrogen and nitrogen oxides when burned.

Magnesium-based

The recovery process used in magnesium-based sulfite pulping the "Magnefite" process is well developed.[8] The concentrated brown liquor is burned in a recovery boiler, producing magnesium oxide and sulfur dioxide, both of which are recovered from the flue gases. Magnesium oxide is recovered in a wet scrubber to give a slurry of magnesium hydroxide.

MgO + H2O → Mg(OH)2

This magnesium hydroxide slurry is then used in another scrubber to absorb sulfur dioxide from the flue gases producing a magnesium bisulfite solution that is clarified, filtered and used as the pulping liquor.

Mg(OH)2 + 2 SO2 → Mg(HSO3)2

Sodium-based

Sodium-based processes use a recovery system similar to that used in the kraft recovery process, except that there is no "lime cycle".

Applications

The sulfite process is acidic and one of the drawbacks is that the acidic conditions hydrolyze some of the cellulose, which means that sulfite pulp fibers are not as strong as kraft pulp fibers. The yield of pulp (based on wood used) is higher than for kraft pulping and sulfite pulp is easier to bleach.

Commodity

Sulfite pulp remains an important commodity, especially for specialty papers and as a source of cellulose for non-paper applications. It is used to make fine paper, tissue, glassine.[9] and to add strength to newsprint.

Dissolving pulp

Main article: Dissolving pulp

A special grade of bleached sulfite pulp is known as dissolving pulp[10] which is the raw material for a wide variety of cellulose derivatives, for example rayon, cellophane, cellulose acetate and methylcellulose.

Rayon is a reconstituted cellulose fiber used to make many fabrics.

Cellophane is a clear reconstituted cellulose film used in wrapping and windows in envelopes.

Cellulose acetate was used to make flexible films for photographic use, computer tapes and so on and also to make fibers.

Methylcellulose and other cellulose ether derivatives are used in a wide range of everyday products from adhesives to baked goods to pharmaceuticals.[11]

Byproducts

Sulfite pulping is generally less destructive than kraft pulping, so there are more usable byproducts.

Lignosulfonates

Chief among sulfite process byproducts are lignosulfonates, which find a wide variety of uses whereas relatively inexpensive agent is needed to make a water dispersion of a water-insoluble material. Lignosulfonates are used in tanning leather, making concrete, drilling mud, drywall and so on.[12]

Oxidation of lignosulfonates was used to produce vanillin (artificial vanilla), and this process is still used by one supplier (Borregaard, Norway) while all North American production by this route ceased in the 1990s.[13]

Other byproducts

Acid hydrolysis of hemicelluloses during sulfite pulping produces monosaccharides, predominantly mannose for softwoods and xylose for hardwoods,[1] which can be fermented to produce ethanol.

See also

References

  1. 1 2 3 4 E. Sjöström (1993). Wood Chemistry: Fundamentals and Applications. Academic Press. ISBN 0-12-647480-X.
  2. 1 2 3 4 Biermann, Christopher J. (1993). Essentials of Pulping and Papermaking. San Diego: Academic Press, Inc. ISBN 0-12-097360-X.
  3. ↑ "History of Paper". Retrieved 2007-10-08.
  4. ↑ "Swedish, German mills phase out sulfite". Pulp and Paper. January 1997. Retrieved 2007-10-08.
  5. ↑ "Wisconsin sulfite mill shuts down 2005". Retrieved 2007-10-07.
  6. ↑ Friederich, Steven (September 25, 2006). "Living on borrowed time its whole life (Weyerhauser sulfite mill)". The Daily World. Retrieved 2007-10-08.
  7. ↑ Chemrec web site
  8. ↑ "Magnefite process". Retrieved 2007-10-11.
  9. ↑ "Grades and uses of paper". Retrieved 2007-10-12.
  10. ↑ "Dissolving pulp by the sulfite process". Retrieved 2007-10-12.
  11. ↑ "Applications for Methocel cellulose ethers from Dow Chemical". Retrieved 2007-10-12.
  12. ↑ "Uses of lignosulfonates". Retrieved 2007-10-07.
  13. ↑ Hocking, Martin B. (September 1997). "Vanillin: Synthetic Flavoring from Spent Sulfite Liquor" (PDF). Journal of Chemical Education. 74 (9): 1055. Bibcode:1997JChEd..74.1055H. doi:10.1021/ed074p1055. Retrieved 2006-09-09.
This article is issued from Wikipedia - version of the 11/12/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.